Kraft Paper
100% Virgin Long Fibre Sack Kraft Paper
Produced in PMI With maximum Deckle 2280 mm
| No. | Term | Unit, SI System | Value | SD | Standard | ||||
|---|---|---|---|---|---|---|---|---|---|
| 1. | Basis Grammage | g/m2 | 45 | 50 | 60 | 70 | 80 | +/-3 g/m2 | ISO 536 |
| 2. | Tensile Strength | KN/m | |||||||
| MD | 4,6 | 5,2 | 6,2 | 7,0 | 7,8 | 7,5% | ISO 1924-2 | ||
| CD | 2,0 | 2,2 | 2,6 | 3,0 | 3,5 | 7,5% | |||
| 3. | Stretch at Break | % | |||||||
| MD | 1,8 | 1,8 | 1,8 | 1,8 | 1,8 | 7,5% | ISO 1924-2 | ||
| CD | 6,0 | 6,0 | 6,0 | 5,8 | 5,8 | 7,5% | 4. | Tensile Energy Absorption ( TEA ) | J/m2 |
| MD | 54 | 60 | 72 | 7,0 | 96 | 7,5% | ISO 1924-2 | ||
| CD | 76 | 85 | 102 | 3,0 | 136 | 7,5% | 5. | Tensile Energy Absorption Index ( TEA Index ) | J/g |
| MD | 1,2 | 1,2 | 1,2 | 1,2 | 1,2 | 7,5% | ISO 1924-2 | ||
| CD | 1,7 | 1,7 | 1,7 | 1,7 | 1,7 | 7,5% | 6. | Tear Strength | mN |
| MD | 450 | 550 | 660 | 840 | 960 | 7,5% | ISO 1974 | ||
| CD | 520 | 650 | 780 | 1000 | 1120 | 7,5% | |||
| 7. | Wire Side Surface Water Absorption (COBB 60) | g/m2 | 25 | 25 | 30 | 30 | 30 | 5,0% | ISO 535 |
| 8. | Porosity (Gurley) | s | 20 | 20 | 20 | 20 | 20 | 10,0% | ISO 5636-5 |
| 9. | Moisture Content | % of weight | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | ISO 287 | |
Values are tested at 23 ºC and 50 % RH. Maximum limits by “Average-2SD”
100% Virgin Long Fibre Sack Kraft Paper
Produced in PMI With maximum Deckle 2280 mm
| No. | Term | Unit, SI System | Value | SD | Standard | ||||
|---|---|---|---|---|---|---|---|---|---|
| 1. | Basis Grammage | g/m2 | 60 | 70 | 80 | 90 | 100 | +/-3 g/m2 | ISO 536 |
| 2. | Tensile Strength | KN/m | |||||||
| MD | 4,6 | 5,2 | 6,2 | 7,0 | 7,8 | 7,5% | ISO 1924-2 | ||
| CD | 2,0 | 2,2 | 2,6 | 3,0 | 3,5 | 7,5% | |||
| 3. | Stretch at Break | % | |||||||
| MD | 1,8 | 1,8 | 1,8 | 1,8 | 1,8 | 7,5% | ISO 1924-2 | ||
| CD | 6,0 | 6,0 | 6,0 | 5,8 | 5,8 | 7,5% | 4. | Tensile Energy Absorption ( TEA ) | J/m2 |
| MD | 54 | 60 | 72 | 7,0 | 96 | 7,5% | ISO 1924-2 | ||
| CD | 76 | 85 | 102 | 3,0 | 136 | 7,5% | 5. | Tensile Energy Absorption Index ( TEA Index ) | J/g |
| MD | 1,2 | 1,2 | 1,2 | 1,2 | 1,2 | 7,5% | ISO 1924-2 | ||
| CD | 1,7 | 1,7 | 1,7 | 1,7 | 1,7 | 7,5% | 6. | Tear Strength | mN |
| MD | 450 | 550 | 660 | 840 | 960 | 7,5% | ISO 1974 | ||
| CD | 520 | 650 | 780 | 1000 | 1120 | 7,5% | |||
| 7. | Wire Side Surface Water Absorption (COBB 60) | g/m2 | 25 | 25 | 30 | 30 | 30 | 5,0% | ISO 535 |
| 8. | Porosity (Gurley) | s | 20 | 20 | 20 | 20 | 20 | 10,0% | ISO 5636-5 |
| 9. | Moisture Content | % of weight | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | ISO 287 | |
Values are tested at 23 ºC and 50 % RH. Maximum limits by “Average-2SD”
100% Virgin Long Fibre Sack Kraft Paper
Produced in PMI With maximum deckle 3660/3060mm
| No. | Term | Unit, SI System | Value | SD | Standard | ||||
|---|---|---|---|---|---|---|---|---|---|
| 1. | Basis Grammage | g/m2 | 60 | 70 | 80 | 90 | 100 | +/-3 g/m2 | ISO 536 |
| 2. | Tensile Strength | KN/m | |||||||
| MD | 5,0 | 5,8 | 6,6 | 7,4 | 8,7 | 7,5% | ISO 1924-2 | ||
| CD | 2,7 | 3,4 | 3,4 | 4,2 | 4,4 | 7,5% | |||
| 3. | Stretch at Break | % | |||||||
| MD | 1,9 | 2,2 | 2,2 | 2,2 | 2,2 | 7,5% | ISO 1924-2 | ||
| CD | 7,0 | 7,0 | 7,0 | 7,0 | 7,7 | 7,5% | 4. | Tensile Energy Absorption ( TEA ) | J/m2 |
| MD | 62 | 80 | 95 | 100 | 113 | 7,5% | ISO 1924-2 | ||
| CD | 135 | 155 | 172 | 193 | 206 | 7,5% | 5. | Tensile Energy Absorption Index ( TEA Index ) | J/g |
| MD | 1,0 | 1,1 | 1,1 | 1,1 | 1,1 | 7,5% | ISO 1924-2 | ||
| CD | 2,2 | 2,2 | 2,2 | 2,2 | 2,2 | 7,5% | 6. | Tear Strength | mN |
| MD | 900 | 1080 | 1240 | 1395 | 1600 | 7,5% | ISO 1974 | ||
| CD | 1055 | 1225 | 1400 | 1575 | 1800 | 7,5% | |||
| 7. | Wire Side Surface Water Absorption (COBB 60) | g/m2 | 30 | 30 | 30 | 30 | 30 | 5,0% | ISO 535 |
| 8. | Porosity (Gurley) | s | 16 | 16 | 16 | 16 | 16 | 10,0% | ISO 5636-5 |
| 9. | Moisture Content | % of weight | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | ISO 287 | |
Values are tested at 23 ºC and 50 % RH. Maximum limits by “Average-2SD”
100% Virgin Long Fibre SEMI-EXTENSIBLE Sack Kraft Paper
Produced in PMI With maximum deckle 3660/3060 mm
| No. | Term | Unit, SI System | Value | SD | Standard | ||||
|---|---|---|---|---|---|---|---|---|---|
| 1. | Basis Grammage | g/m2 | 70 | 80 | 90 | 100 | 110 | +/-3 g/m2 | ISO 536 |
| 2. | Tensile Strength | KN/m | |||||||
| MD | 5,5 | 6,0 | 7,2 | 7,3 | 7,4 | 7,5% | ISO 1924-3 | ||
| CD | 3,5 | 3,7 | 4,1 | 4,6 | 4,8 | 7,5% | |||
| 3. | Stretch at Break | % | |||||||
| MD | 6,0 | 6,0 | 6,0 | 6,0 | 6,0 | 5,0% | ISO 1924-3 | ||
| CD | 7,0 | 7,0 | 7,0 | 7,0 | 7,7 | 7,5% | 4. | Tensile Energy Absorption ( TEA ) | J/m2 |
| MD | 190 | 210 | 240 | 250 | 257.5 | 7,5% | ISO 1924-3 | ||
| CD | 155 | 180 | 190 | 205 | 220 | 7,5% | 5. | Tensile Energy Absorption Index ( TEA Index ) | J/g |
| MD | 2,7 | 2,7 | 2,6 | 2,5 | 2,3 | 7,5% | ISO 1924-3 | ||
| CD | 2,2 | 2,2 | 2,1 | 2,05 | 2,0 | 7,5% | 6. | Tear Strength | mN |
| MD | 1050 | 1200 | 1350 | 1500 | 1650 | 7,5% | ISO 1974 | ||
| CD | 1330 | 1520 | 1710 | 1900 | 2090 | 7,5% | |||
| 7. | Wire Side Surface Water Absorption (COBB 60) | g/m2 | 30 | 30 | 30 | 30 | 30 | 5,0% | ISO 535 |
| 8. | Porosity (Gurley) | s | 18 | 18 | 18 | 18 | 18 | 10,0% | ISO 5636-5 |
| 9. | Moisture Content | % of weight | 5,5-7,5 | 5,5-7,5 | 5,5-7,5 | 5,5-7,5 | 5,5-7,5 | ISO 287 | |
Values are tested at 23 ºC and 50 % RH. Maximum limits by “Average-2SD”
100% Virgin Long Fibre Sack Kraft Paper
Produced in PMI With maximum deckle 3660/3060mm
| No. | Term | Unit, SI System | Value | SD | Standard | ||||
|---|---|---|---|---|---|---|---|---|---|
| 1. | Basis Grammage | g/m2 | 110 | 120 | 130 | 140 | 150 | +/-3 g/m2 | ISO 536 |
| 2. | Tensile Strength | KN/m | |||||||
| MD | 9.7 | 10.7 | 11.6 | 12.7 | 13.4 | 7,5% | ISO 1924-2 | ||
| CD | 4.7 | 5.0 | 5.4 | 5.7 | 5.9 | 7,5% | |||
| 3. | Stretch at Break | % | |||||||
| MD | 2.1 | 2.1 | 2.1 | 2.1 | 2.1 | 7,5% | ISO 1924-2 | ||
| CD | 7,0 | 7,0 | 7,0 | 7,0 | 7,0 | 7,5% | 4. | Tensile Energy Absorption ( TEA ) | J/m2 |
| MD | 123.5 | 134 | 159.5 | 175 | 185 | 7,5% | ISO 1924-2 | ||
| CD | 226.5 | 242 | 247.0 | 259.5 | 278 | 7,5% | 5. | Tensile Energy Absorption Index ( TEA Index ) | J/g |
| MD | 1.1 | 1.1 | 1.2 | 1.2 | 1.2 | 7,5% | ISO 1924-2 | ||
| CD | 2.0 | 2.0 | 1.9 | 1.85 | 1.85 | 7,5% | 6. | Tear Strength | mN |
| MD | 1800 | 2000 | 2200 | 2400 | 2600 | 7,5% | ISO 1974 | ||
| CD | 2000 | 2250 | 2500 | 2750 | 3000 | 7,5% | |||
| 7. | Wire Side Surface Water Absorption (COBB 60) | g/m2 | 30 | 30 | 30 | 30 | 30 | 5,0% | ISO 535 |
| 8. | Porosity (Gurley) | s | 16 | 14 | 14 | 12 | 12 | 10,0% | ISO 5636-5 |
| 9. | Moisture Content | % of weight | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | 6,5-8,5 | ISO 287 | |
Values are tested at 23 ºC and 50 % RH. Maximum limits by “Average-2SD”
100% Virgin Long Fibre SEMI-EXTENSIBLE Sack Kraft Paper
Produced in PMI With maximum deckle 3660/3060 mm
| No. | Term | Unit, SI System | Value | SD | Standard | ||
|---|---|---|---|---|---|---|---|
| 1. | Basis Grammage | g/m2 | 120 | 130 | 140 | +/-3 g/m2 | ISO 536 |
| 2. | Tensile Strength | KN/m | |||||
| MD | 8,0 | 8,7 | 9,4 | 7,5% | ISO 1924-3 | ||
| CD | 5,4 | 5,9 | 6,3 | 7,5% | |||
| 3. | Stretch at Break | % | |||||
| MD | 6,0 | 6,0 | 6,0 | 7,5% | ISO 1924-3 | ||
| CD | 7,0 | 7,0 | 7,0 | 7,5% | 4. | Tensile Energy Absorption ( TEA ) | J/m2 |
| MD | 276 | 286 | 294 | 7,5% | ISO 1924-3 | ||
| CD | 234 | 245 | 255 | 7,5% | 5. | Tensile Energy Absorption Index ( TEA Index ) | J/g |
| MD | 2,3 | 2,2 | 2,1 | 7,5% | ISO 1924-3 | ||
| CD | 1,95 | 1,9 | 1,85 | 7,5% | 6. | Tear Strength | mN |
| MD | 1830 | 1985 | 2135 | 7,5% | ISO 1974 | ||
| CD | 2250 | 2440 | 2625 | 7,5% | |||
| 7. | Wire Side Surface Water Absorption (COBB 60) | g/m2 | 30 | 30 | 30 | 5,0% | ISO 535 |
| 8. | Porosity (Gurley) | s | 16 | 16 | 16 | 10,0% | ISO 5636-5 |
| 9. | Moisture Content | % of weight | 5,5-7,5 | 5,5-7,5 | 5,5-7,5 | ISO 287 | |
Values are tested at 23 ºC and 50 % RH. Maximum limits by “Average-2SD”
100% Virgin Long Fibre Fully-Extensible Sack Kraft Paper
Produced in PMI With maximum deckle 3660/3060 mm
| No. | Term | Unit, SI System | Value | SD | Standard | ||
|---|---|---|---|---|---|---|---|
| 1. | Basis Grammage | g/m2 | 70 | 80 | 90 | +/-3 g/m2 | ISO 536 |
| 2. | Tensile Strength | KN/m | |||||
| MD | 5,3 | 5,8 | 6,4 | 7,5% | ISO 1924-3 | ||
| CD | 3,5 | 3,8 | 4,5 | 7,5% | |||
| 3. | Stretch at Break | % | |||||
| MD | 7,5 | 7,5 | 7,5 | 7,5% | ISO 1924-3 | ||
| CD | 7,0 | 7,0 | 7,0 | 7,5% | 4. | Tensile Energy Absorption ( TEA ) | J/m2 |
| MD | 200 | 220 | 250 | 7,5% | ISO 1924-3 | ||
| CD | 160 | 180 | 200 | 7,5% | 5. | Tensile Energy Absorption Index ( TEA Index ) | J/g |
| MD | 2,9 | 2,8 | 2,8 | 7,5% | ISO 1924-3 | ||
| CD | 2,3 | 2,2 | 2,2 | 7,5% | 6. | Tear Strength | mN |
| MD | 1050 | 1200 | 1350 | 7,5% | ISO 1974 | ||
| CD | 1330 | 1520 | 1710 | 7,5% | |||
| 7. | Wire Side Surface Water Absorption (COBB 60) | g/m2 | 30 | 30 | 30 | 5,0% | ISO 535 |
| 8. | Porosity (Gurley) | s | 18 | 18 | 18 | 10,0% | ISO 5636-5 |
| 9. | Moisture Content | % of weight | 5,5-7,5 | 5,5-7,5 | 5,5-7,5 | ISO 287 | |
Values are tested at 23 ºC and 50 % RH. Maximum limits by “Average-2SD”